ANYCUBIC Water-Wash Resin 2.0 is a transparent water-washable photopolymer resin for LCD/DLP UV-curing 3D printers. It enables easy cleaning with water without IPA, offers high print accuracy, lower odor, higher crack resistance, and protection against yellowing for long-lasting, aesthetic, and detailed prints.
ANYCUBIC Water-Wash Resin 2.0 (transparent) is a light-curable material designed for 3D printing using LCD and DLP technologies. Thanks to its hydrophilically modified formulation, post-processing of models is significantly more convenient – leftover resin can be removed after printing with water only, saving time and operating costs (no need to use isopropyl alcohol).
The material is designed for detailed and accurate prints with a smooth surface while also providing higher mechanical durability. Low volume shrinkage helps maintain dimensional accuracy, and the improved formula reduces the risk of yellowing, so models look good even after a longer time.
Main advantages:
- Water cleaning thanks to the hydrophilic formulation (no IPA; IPA can also be used if needed)
- Higher crack resistance and good strength after curing
- High accuracy and the ability to reproduce fine details (stated accuracy up to 0.15 mm)
- Anti-yellowing protection for a long-lasting aesthetic appearance
- Stable printing thanks to low viscosity and better adhesion to the build plate
- Wide compatibility with UV curing in the 365–405 nm range (typically 405 nm)
Specifications
- Manufacturer
- ANYCUBIC
- Model
- Water-Wash Resin 2.0
- Color
- Transparent
- Material
- Light-curable resin modified with hydrophilic groups
- Wavelength
- 365–405 nm
- Viscosity
- 190–230 mPa·s (25 °C)
- Density
- 1.07–1.09 g/cm³
- Hardness
- 82–85 HD
- Tensile strength
- 38–43 MPa
- Elongation at break
- 16–22 %
- Flexural modulus
- 48–60 MPa
- Flexural strength
- 2300–3000 MPa
- Young’s modulus
- 1100–1300 MPa
- Izod impact strength
- 133 J/m
- Volume shrinkage
- 2.2–5.5 %
- Printing temperature
- 20–50 °C
- Recommended ambient temperature during printing
- 20–40 °C
- Exposure time for first layer
- 25–40 s
- Exposure time for standard layer
- 2–2.5 s
- Cleaning agent
- 95% IPA / water
- Cleaning time
- 95% IPA: ≤3 min; water: medium, ≤5 min
- UV wavelength during curing
- 405 nm
- Curing temperature
- 18–30 °C
- UV intensity
- 25 000–30 000 µW/cm²
- Curing time
- 3 min
- Weight
- 1 kg